Preparation of Metal Toughened Ceramic Tool Material

Couverture du livre « Preparation of Metal Toughened Ceramic Tool Material » de Suprakash Mondal aux éditions Editions Universitaires Europeennes
Résumé:

The present work is aimed to develop metal toughened alumina composite which will be used as a cutting tool material, primarily by addition of silver, then microstructural characterization and property measurement of the developed composite. In the work a chemical synthesis using the sol-gel... Voir plus

The present work is aimed to develop metal toughened alumina composite which will be used as a cutting tool material, primarily by addition of silver, then microstructural characterization and property measurement of the developed composite. In the work a chemical synthesis using the sol-gel method was carried-out to prepare alumina powder from aluminium nitrate Al (NO3)3,9H2O. Then AgNO3 was well mixed with the prepared -Al2O3 powder in aqueous solution followed by evaporation and heating, to get 5 and 12 volume percent of Ag in the Al2O3-Ag mixture. A conventional powder metallurgical route was followed to prepare Al2O3-Ag composite pellets. First PVA was added as binder with the mixture, and then the powder was compacted in a circular shaped hole die-punch assembly at certain uni-axial pressure for the samples in a hand press to prepare disc pellets of size 16 mm diameter and thickness of ~6mm and ~3mm . The pellets were first dried at 500°C for 2 hours to burn off the PVA, then pre- sintered at 950°C for 2 hours and finally sintered at 1600°C for 2 hours as soaking time in a furnace.

Donner votre avis

Donnez votre avis sur ce livre

Pour donner votre avis vous devez vous identifier, ou vous inscrire si vous n'avez pas encore de compte.

Récemment sur lecteurs.com

Les livres les mieux notés cette semaine